Pro-fax HP525J is a polypropylene homopolymer typically used in the production of biaxially oriented polypropylene films (BOPP). The product is suitable for metallizable film, both as monolayer and in coextruded structures. It contains a standard processing stabilization but does not contain any slip, antiblocking agents and no Calcium Stearate is intentionally added. Pro-fax HP525J offers good optical, easy processing and very good film profile. Typical applications are BOPP packaging films and Solid Phase Thermoforming sheets.
Pro-fax HP525J
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 3.0 g/10 min |
| Density (23 °C) | 0.90 g/cm³ |
| Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) | 218000 psi |
| Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A) | 1500 MPa |
| Tensile Strength at Yield (2 in/min) | 5100 psi |
| Tensile Strength at Yield (50 mm/min) | 35 MPa |
| Tensile Elongation at Yield | 11 % |
| Notched Izod Impact Strength (73 °F, Method A) | 0.8 ft-lb/in |
| Notched Izod Impact Strength (23 °C, Method A) | 43 J/m |
| Deflection Temperature Under Load (66 psi, Unannealed) | 203 °F |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 95 °C |
Technical Data Sheet
Technical Data SheetProcess
BOPP, Thermoforming
Resin
Polypropylene, Homopolymer
Applications
Food Packaging Film, Thermoformed Food Containers